Latest informations and news about the Rubber industry and all about elastomer,vulcanisate,rubber compound,rubber processing,injection moulding,extrusion,natural rubber NR,synthetic rubber,elasticity,latex,hard rubber,carbon black,polybutadiene BR,polyisoprene IR,styrene butadiene rubber SBR,rubber,solution-SBR,acrylonitrile-butadiene rubber NBR,ethylene-propylene rubber EPM,ethylene-propylene-diene rubber EPDM,butyl rubber IIR,halogen butyl rubber,chloroprene CR,fluorocarbon rubber FKM,acrylate rubber ACM,polysulfide rubber,silicone rubber,calendering,blow moulding,Ziegler-Natta catalysts ,tyre tread,tyre sidewall,tyre,seals,profile,cable sheathing,liquid silicone rubber LSR,rubber-metal articles,hose,PEEK,Arburg,BASF,Bayer,Desma,DuPont,Engel,Evonik,Feddersen,Ferromatik Milacron,FKuR,Haitian,HF Mixing Group,Hilma-Römheld,Hoffmann Mineral,Kraiburg,KraussMaffei Berstorff,Lanxess,LWB Steinl,Maplan,Rado,Reifenhäuser,Rio Tinto,Rubicon,Ticona,Troester,Uth,Victrex,Wacker,Zeon,Zwick,gasket,ANRPC,DKG,IRSG,IISRP,WDK,Elastomer Cluster Germany,DIK,Rapra

Only for 12,90 EUR

Reinforcement of diene elastomers by organically modifed layered silicates

von Maurizio Galimberti, Stanislao Senatore, Angela Lostritto, Luca Giannini, Lucia Conzatti, Giovanna Costa, Gaetano Guerra

Nanocomposites were prepared based on diene rubbers and layered clays modified with an alkyl quaternary ammonium cation (organoclay). A diene rubber, either polybutadiene, or synthetic or naturally occurring polyisoprene or styrene-butadiene copolymer, was melt-blended with either a preformed organoclay or with a mixture of pristine clay and ammonium cation.

Besides isolated lamellae, nanocomposites showed the presence of crystalline organoclays with intercalated organic layers made only by low molecular mass substances, essentially the ammonium cation, and no evidences for the intercalation of polymer chains were observed.

Dynamic mechanical properties of sulphur-cured compounds with carbon black as the main filler and a minor amount of organoclay were investigated. The organoclay was found to bring about a reduction of Mooney viscosity, an increase of storage modulus at low temperature as well as an increase of thermoplasticity.